Abstract
Zn1-xCoxO thin films on sapphire (0001) substrates were synthesized by laser molecular beam epitaxy (LMBE) method at various temperatures under a work ambient pressure of 5.0 x 10-5Pa condition. X-ray diffraction (XRD) spectra, UV–visible transmission spectra and X-ray photoelectron spectroscopy (XPS), photoluminescence (PL) spectra were employed to characterize the properties of samples. All samples were of wurtzite hexagonal structure with the preferential c-axis-orientation. Co2+ions incorporated into ZnO lattice and substituted for Zn2+ions. ZnLMM Auger spectrum implied Zn interstitials existed in sample. The optical transmission of all samples was relatively high in visible region. Two PL emission peaks located at 418 nm and 490 nm were assigned to the electron transition from the Zn interstitials to the top of the valence band and from the Zn interstitials to the Zn vacancies, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.