The coexistence of the magnetic and the electrical properties in lanthanum (La)-modified bismuth ferrite (Bi1−xLaxFeO3, x=0.05, 0.1, 0.15, and 0.2) ceramics was studied and compared with those of bismuth ferrite (BiFeO3). The presence of a small secondary phase of BiFeO3 (arises due to excess Bi2O3) was removed on La substitution at the Bi site, as observed in x-ray diffraction (XRD). The effect of La substitution on dielectric constant, loss tangent, and remnant polarization of the samples was studied in a wide range of temperature (77–400K) and frequency (1kHz–1MHz). The variation of magnetization, coercive field, and exchange bias with temperature (2–300K) and La concentration were investigated. These changes in the magnetic parameters with La doping along with those of the electron magnetic resonance parameters measured at 300K and 9.28GHz are understood in terms of increase in the magnetic anisotropy and magnetization. These results also show that stabilization of crystal structure and nonuniformity in spin cycloid structure by La substitution enhances the multiferroic properties of BiFeO3.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.