Structural and multiferroic properties of Ba2+ doped BiFeO3 nanoparticles synthesized via sol-gel method

Abstract

Ba2+ doped Bismuth ferrite nanoparticles having general formula Bi1-xBaxFeO3 (where, x = 0.00 and 0.20) were successfully synthesized by sol gel method, using nitrates as a starting material. Ethylene glycol was used as a solvent. The synthesized powder was sintered at 650°C for 4 hours to obtain pure phase BFO. Leaching with dilute nitric acid (HNO3) and distilled water (H2O) is done to remove the impurities. The structural, morphological, magnetic and ferroelectric properties were systematically investigated using standard characterization techniques like X-ray diffraction (XRD), Field Emission Scanning Electron Microscopy (FE-SEM) and room temperature magnetic behavior of the samples was studied using pulse field hysteresis loop tracer technique showing increase in saturation magnetizaion. P-E loop confirms the ferroelectric behavior of prepared nanoparticles. The coexistence of ferromagnetic and ferroelectric hysteresis loops in BFO and Bi0.8Ba0.2FeO3 nanoparticles samples at room temperature; it indicates that the samples are potential candidates for information storage and spintronics devices. The increase in magnetic properties may be important for practical application at room temperature.