Dy 1 − x Pr x ( Fe 0.35 Co 0.55 B 0.1 ) 2 (0⩽x⩽1) Laves compounds with a cubic MgCu2-type structure were synthesized by arc melting and subsequent annealing. The lattice parameter of the Laves compounds linearly increases, while the Curie temperature TC decreases with increasing Pr content. The saturation magnetization Ms at 5K or 295K for the Dy1−xPrx(Fe0.35Co0.55B0.1)2 alloys decreases to reach a minimum, then increases with increasing Pr content. The composition for magnetic moment compensation is about x=0.55 at 295K and x=0.65 at 5K, respectively. The magnetostriction λ‖ or λ⊥ at room temperature was investigated either parallel or perpendicular to the applied field using a standard strain gauge technique.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.