Abstract
The influence of composition on the structural ordering and magnetism in the V x Nb 1+ y S 2 system has been investigated by X-ray diffraction and magnetic measurements. Stoichiometric V 1/3NbS 2 did not exhibit the structural ordering of vanadium between the NbS 2 layers. In the ordered structure, the vanadium composition deviated from the ideal value of x = 1 3 to both higher and lower values, while the niobium composition was in the range of 0.05⩽ y⩽0.18. Excess niobium, y>0, is thought to play an essential role in the structural ordering in this system. For samples with excess niobium and ordered structures, a magnetic transition was observed at 20–50 K, depending on the composition. The spontaneous magnetization of 3–5×10 −3 μ B/V atom is thought to be intrinsic to this system. The magnetization curves consisted of a constant and a proportional parts of the magnetic field, which correspond to the spontaneous magnetization and high-field susceptibility, respectively. The magnetization curves and the temperature dependencies of the high-field susceptibility were quite similar to those of the canted antiferromagnetic NiS 2. A correlation between the structural and magnetic ordering is suggested.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.