Abstract

The Pb(Zr,Ti)O 3 thin films with single (111) oriented perovskite phase and excellent electrical properties have been prepared by annealing the as-deposited samples. The orientation of crystals depends strongly on both the deposition temperature and annealing temperature. The sample annealed at 606°C has the best (111) orientation. When the sample is annealed at lower temperature, the relative content of (111) oriented perovskite phase decreases quickly with increase of deposition temperature. The deposition temperature has little effects on the orientation when the sample is annealed at higher temperature. The effects of deposition temperature and annealing temperature on the crystallographic structures and electrical properties of PZT thin films were investigated in this paper. The sample deposited at 285°C and annealed at 606°C has the maximum value of polarization, which displays excellent ferroelectric properties. The typical P r and P s values are 57 and 101 μC/cm 2, respectively.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.