Abstract
Ceramic solid solutions Bi4MnxV2–xO11–(x/2)–δ in the composition range 0.07 ≤ x ≤ 0.30 were obtained by solid state synthesis. Structural investigations were carried out by using a combination of FT-IR and powder X-ray diffraction technique. Polymorphic transitions (β↔γ and γ′↔γ) were detected by DTA and variation in the Arrhenius plots of conductivity. The solid solutions with composition 0.07 ≤ x ≤ 0.17 are isostructural with the orthorhombic β-phase, and those with x ≤ 0.30 represent tetragonal γ-phase. With increasing Mn concentration, the conductivity of solid solutions increases from 3.684×10-6 (x = 0.07) to 2.467×10-5 (x = 0.17). AC impedance plots show that the conductivity is mainly due to the grain contribution which is evident in the enhanced short range diffusion of oxide ion vacancy in the grains with increasing temperature.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.