Abstract
B2O3 and Li2O (B/L)-added Ba0.6Sr0.4TiO3 (BST) ceramics sintered at 940 °C exhibited a dense microstructure with large grains. The amount of B/L additive was 4.5 wt% with a B/L ratio of 1.5:1. The B/L-related liquid phase assisted the densification of the BST ceramics. This BST ceramic displayed a large dielectric constant (εr) of 2834 with a low dielectric loss (tan δ) of 0.21% at 1.0 MHz. It also displayed a large tunability (28.2% at 10 kV/cm) and a high figure of merit (FOM) of 134. BST thick-films were synthesized using the tape casting method. The thick-film densified at 940 °C exhibited a large tunability of 18.7% at 10.0 kV/cm and an FOM of 208; these are higher than the values reported in the literature. Multilayer ceramics (MLCs) consisting of five layers of 40-μm-thick BST thick-films and Ag electrodes were also fabricated at 940 °C. No diffusion occurred between the Ag electrode and BST thick-film. A large tunability of 67.6% at 52 kV/cm with a high FOM of 294 was obtained from this MLC. This verified that the B/L-added BST ceramic is effective for application in tunable multilayer devices.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.