Abstract
Structural and dielectric properties of (1−x)BaTiO3–xBi(Mg1/2Ti1/2)O3 (x = 0.1–0.5) were investigated to understand the binary system and utilize it for high‐voltage, high energy density capacitors. The solubility limit for Bi(Mg1/2Ti1/2)O3 in a BaTiO3 perovskite was between x = 0.4 and x = 0.5. A phase with pseudocubic symmetry was formed for x = 0.1–0.4; a secondary phase developed at x = 0.5. Dielectric measurements showed highly diffusive and dispersive relaxor‐like characteristics from 10 to 40 mol% of Bi(Mg1/2Ti1/2)O3. These compositions also showed high relative permittivity with low‐temperature coefficients of permittivity over a wide range of temperatures −100°C–600°C. Relaxation behavior was quantitatively investigated using the Vogel–Fulcher model, which revealed the activation energy of 0.17–0.22 eV. Prototyped multilayer capacitors of 18 mm × 17 mm × 4 mm dimensions with a capacitance of 12.5 nF at 1 kHz were successfully constructed and demonstrated multiple charge–discharge characteristics up to 10 kV.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.