Abstract
Atomic structures of crystalline (c-)HoFe 2D 3.6 and amorphous (a-)HoFe 2D 3.0 prepared by deuterium absorption of the C15 Laves phase compound HoFe 2 were studied by X-ray and neutron diffraction techniques and these were compared with previous results for c- and a-TbFe 2D x . The structural parameters such as an interatomic distance and a coordination number are qualitatively in agreement with those for c- and a-TbFe 2D x . Namely, a marked difference was observed in the arrangement of metal atoms in a-HoFe 2D 3.0 compared to that in c-HoFe 2D 3.6 from interatomic distances and coordination numbers and there are clusters of Fe and Ho atoms in a-HoFe 2D x . RDF( r)s observed by the neutron diffraction indicated that the D atoms occupy tetrahedral sites consisting of 2Ho+2Fe in c-HoFe 2D 3.6, while the D atoms occupy selectively tetrahedral sites consisting mainly of Ho atoms in a-HoFe 2D 3.0 because of strong affinity between D and Ho atoms. The reverse Monte Carlo (RMC) modeling method was employed to visualize a three-dimensional atomic arrangement by using combined X-ray and neuron diffraction data of RFe 2D x (R: Ho, Tb). Chemical fluctuation was visually observed in the RMC configurations. Moreover, it was found that about 40% of the D atoms occupy sites consisting of 4R.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.