Abstract
Perovskite crystal structure is found in many ionic solids like CaTiO3, BaTiO3 and Lead Zirconate Titanates (PZT). In this structure off-center position of cations in oxygen octahedral causes polarization and produces direct and indirect piezoelectric responses in ceramic materials that are suitable for many ultrasonic applications. In the present study 9% Sr doped PZT ceramics were prepared and their dielectric and piezoelectric properties measured. X ray Diffraction (XRD) analysis of calcined powders demonstrated a decrease in the PbO content during the calcination stage at 850 degrees C. This was counterbalanced by adding excess PbO at the time of preparation of mixtures. Sintering was carried out at 1200 degrees C for 2 hours in lead rich atmosphere. The properties achieved were Dielectric Constant (K) = 1440, Tangent Loss (Tan delta) = 0.0062, Charge Coefficient (d33) = 335 pC/N and density = 7.55 g/cm3. SEM analysis of sintered samples demonstrated that grain size was 2-3 microm with clean grain boundaries and no large size porosity observed. XRD analysis of sintered pellets exhibited that material prepared was free of any precipitated phase usually harmful for the piezo effect.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.