Strong strain rate effect on the plasticity of amorphous silica nanowires

Abstract

With electron-beam (e-beam) off, in-situ tensile experiments on amorphous silica nanowires (NWs) were performed inside a transmission electron microscope (TEM). By controlling the loading rates, the strain rate can be adjusted accurately in a wide range. The result shows a strong strain rate effect on the plasticity of amorphous silica NWs. At lower strain rate, the intrinsic brittle materials exhibit a pronounced elongation higher than 100% to failure with obvious necking near ambient temperature. At the strain rate higher than 5.23 × 10−3/s, the elongation of the NW decreased dramatically, and a brittle fracture feature behavior was revealed. This ductile feature of the amorphous silica NWs has been further confirmed with the in-situ experiments under optical microscopy while the effect of e-beam irradiation could be eliminated.