Abstract
Gadolinium-oxide nanopowders doped with Yb3+ and Ho3+ ions and co-doped with alkali metal ions (Li+ and Na+) were synthesized via the polymer complex solution method and their up-conversion emission properties are analyzed. Prepared powders were well crystallized in cubic bixbyite structure, without any impurity phases and with an average crystallite size of about 25nm, as shown by X-ray powder diffraction analysis. No adsorbed species on the surface of nanoparticles were detected by infrared measurements. The particle morphology was analyzed by transmission electron microscopy, which revealed agglomerated crystalline nanoparticles with irregular, polygonal-like shapes, having a size in the range from 30 to 50nm. Up-conversion emission properties of Gd2O3:Ho3+,Yb3+ nanopowders were evaluated from photoluminescence emission and decay measurements using 980nm excitation. Two-photon up-conversion processes produced emissions in visible – near infrared spectral range, with the strongest green emission from 5F4,5S2→5I8 Ho3+ electronic transition, and weak red and near infrared from 5F5→5I8 and 5F4, 5S2→5I7 transitions, respectively. In addition, three-photon up-conversion emission was detected in ultra-violet–blue spectral region (5G4→5I8, 3D3→5I6 and 5G5→5I8 transitions). Luminescence measurements were performed on samples with different Ho3+ (0.5 and 1at%) and Yb3+ (2, 4 and 6at%) concentrations to find that 0.5at% of Ho3+ and 2at% of Yb3+ provides the most intense up-conversion emission. The influence of alkali metal (Li+ and Na+) ion co-doping is studied on the sample that showed the most intense up-conversion emission. Increase in the intensity of up-conversion emission is observed for both Li+ and Na+ co-doping. The effect is more pronounced with Li+, where addition of 5at% of Li+ led to more than one order of magnitude emission enhancement. Alkali metal ion co-doping also significantly improved up-conversion color purity through considerably larger increase of green emission compared to red and near infrared.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.