Stress-relaxation heat treatment in FeSiBNb amorphous alloy: Thermal, microstructure, nanomechanical and magnetic texture measurements

Abstract

In the present study, the effect of stress-relaxation treatment (Tstress-relaxation < Tglass transition) on the magnetic texture, nanomechanical properties, and variation of free-volume in FeSiBNb amorphous alloy was investigated using Mössbauer spectroscopy, nanoindentation, dynamic mechanical analysis (DMA), and positron annihilation lifetime spectroscopy (PALS) techniques. It was shown that stress-relaxation treatment slightly improved the magnetic texture by 6% at T≪Tg due to small-scale displacement of atoms whereas the magnetic texture was deteriorated due to thermal treatment at temperatures around the glass transition point (large-scale displacement of atoms). According to nanoindentation results, the hardness (H) and reduced modulus (Er) of the amorphous ribbon increased by 15% and 13%, respectively, after stress-relaxation treatment at 716 K for 5 min. Increasing the stress-relaxation time from 5 min to 60 min at 716 K resulted in decreases in the hardness and reduced modulus which are attributed to the increase of free-volume defects (increase of τ2 lifetime measured by PALS). Transmission electron microscopy (TEM) showed the formation of extremely fine embryos of α-Fe (3–5 nm in size) after stress-relaxation treatment.