Abstract

ABSTRACTThe stress induced failure of passivated aluminum based metallizations is the combined result of the stress induced void nucleation and growth of voids. The present work investigates the dependence of the void nucleation on aging temperature and cooling rate. Narrow Al, Al(0.2%Cu) and Al(2%Si) lines of different widths were fabricated by lift-off and passivated with various thicknesses of Si3N4. After a 400°C anneal, the specimens were cooled directly to the selected aging temperature and aged for up to 1100 hours. Void nucleation was found to occur predominantly during the initial cool-down. The rate of nucleation varied in quite different ways with the combination of aging temperature and cooling rate for the different alloys, which is consistent with a grain boundary sliding controlled nucleation mechanism.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.