Abstract
Boron modified polyvinylsilazane was thermolyzed at 1300°C under argon atmosphere and subsequently spark plasma sintered at 1600°C in vacuum. The material was subjected to highly saline and constant vapor pressure environments individually to understand the influence of chemistry in propagating the subcritical cracks. The failure behavior in chloride environment was compared against humid environment using the data extracted from Raman spectroscopy, the thermodynamic characteristics of the environment and the micro-sized pore concentrations. The implications of the subcritical crack growth were derived by plotting ν–KI graphs for each of the samples to clearly distinguish between the effects of the surrounding mediums. The impulse to crack propagation was found to be resistive with variations in degree of crack growth alternating directly with the changes in porosity, surrounding atmosphere and defect density. The rate of energy dissipation and its hindrance at the crack tip were found to be a major player, among others, in reducing the crack propagation rate.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.