Abstract
AbstractPolyethylene terephthalate (PET) prepolymer containing 0.0 to 0.3 mole percent pentaerythritol was polymerized to an inherent viscosity of 0.63‐0.70 dl/gm by the fluidized bed technique. Rheological studies and gel permeation chromatography (GPC) examination showed the samples to be branched in character. Amorphous films were stretched at 82 and 93°C at elongation rates of 54, 161 and 267 percent‐s−1 using the T. M. Long machine. The extent of stress‐induced crystallization was established by a density determination. The branched samples behaved very similarly to the linear PET material in crystallization and birefringence studies. Neither the percent crystallinity nor the birefringence appears to be a strong function of strain rate over the range 54‐267 percent‐s−1. A cursory examination of the crystallization kinetics of the oriented samples suggests that extent of branching in our samples does not markedly reduce the crystallization rate at annealing temperatures of 180 and 220°C.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.