Stress Analysis and Failure Mechanisms of Plasma-Sprayed Thermal Barrier Coatings

Abstract

Yttria-stabilized zirconia coatings were deposited by plasma spraying and heat-treated at 1100 °C for 50, 100, 150, and 200 h in air, respectively. Mechanical properties including microhardness and Young’s modulus were evaluated using the nanoindentation test. Residual stresses in the ceramic topcoat and the thermally grown oxide (TGO) layer were measured using Raman spectroscopy and photoluminescence piezo-spectroscopy (PLPS) techniques, respectively. The results showed that both the modulus and hardness increased with the thermal exposure time up to 100 h and then gradually decreased. The accumulated tensile stress in the as-sprayed topcoat changed to compressive stress after thermal exposure, and the compressive stress in the topcoat increased with an increase of thermal exposure time up to 150 h. The average compressive stresses in the TGO layer were higher than that of the cross-sectional topcoat, and the measured in-plane compressive stress increased firstly and then gradually decreased with increasing exposure time. The local interface geometry strongly affect the nature and evolution of hydrostatic stresses in the TGO. Finally, the crack initiation and propagation at the topcoat/TGO/bondcoat interface has been discussed with respect to the residual stresses in the plasma-sprayed TBC system.