Abstract
High entropy alloys (HEAs) are facing difficulties in balancing strength and ductility, and till now there is no satisfactory solution. In this paper, the CoCrFeNiNb0.25 HEA with good ductility was strengthened by a face centered cubic (FCC) precipitate after annealing heat treatment. When the CoCrFeNiNb0.25 HEA was annealed at 750 °C, a lath-shaped FCC precipitates with nano basket-weave microstructures appeared and distributed randomly in the proeutectic FCC phase. Due to the precipitation strengthening, the yield stress of the CoCrFeNiNb0.25 HEA almost doubled but its ductility was just slightly damaged.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.