Abstract
PurposeThe purpose of this study is to investigate the effect of standard fire on the strength and microstructure properties of concrete with different strength grades.Design/methodology/approachDifferent strength grades of concrete used for the investigation are M20, M30, M40 and M50. An electrical bogie hearth furnace was developed to simulate the International Standards Organization 834 standard fire curve.Concrete samples were subjected to high temperatures of 925, 1,029, 1,090 and 1,133°C for the duration of 1, 2, 3 and 4 h, respectively, as per standard fire curve. Compressive strength, tensile strength, thermal crack pattern and spalling of heated concrete specimens were evaluated by experimental investigation. Scanning electron microscopy and thermo-gravimetric analysis were performed to investigate the microstructure properties of heated concrete specimens.FindingsTest results indicated reduction in the strength and changes in the microstructure properties of concrete exposed to elevated temperature. The degree of weight and the strength loss were found to be higher for concrete with higher grades. An empirical relation is proposed to determine the residual strength of concrete with different strength grade using regression analysis.Social implicationsResults of this research will be useful for the design engineers to understand the behavior of concrete exposed to elevated temperature as per standard fire.Originality/valueWhen concrete is exposed to elevated temperature, its internal microstructure changes, thereby strength and durability of concrete deteriorates. The performance of concrete with different strength grade exposed to standard fire is well understood. This research’s findings will be useful for the designers to understand more about fire resistance of concrete. A simple relationship is proposed to determine the residual strength of concrete exposed to various durations of heating.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.