Strength and Contaminant Toxicity Leaching Characteristics of MgO-Solidified Silt

Abstract

In this study, MgO as an environmentally friendly silt-solidifying material was first mixed with silt and then carbonized by injection with CO2. The strength and contaminant leaching characteristics of the MgO-solidified silt were studied using unconfined compressive strength and toxicity leaching tests, and the results were compared with those of cement-solidified silt. The unconfined compressive strength of the silt reached 111 kPa with 9% MgO content and a 14 d curing time. The CO2 injection further increased the unconfined compressive strength of the MgO-solidified silt by approximately 25%: the values for MgO-solidified silts without and with a CO2 injection were approximately 60% and 80%, respectively, of those of the cement-solidified silts with the same additive additions. The leaching concentrations of nutrient salts and heavy metal pollutants in the silt decreased with increased MgO content. Compared with the dredged silt, MgO solidification with carbonization reduced the leaching of total nitrogen and total phosphorus by more than 10% and 50%, respectively: these values were approximately 5% points higher than those of cement-solidified silt. Of the heavy metals, the leaching concentration of Ni was reduced the most. This study provides a theoretical basis and technical support for low-carbon treatment and green resource utilization of dredging silt.