Abstract
The strain rate sensitivity of the aluminium alloy AA6061 has been investigated in a conventional grain sized (CG) state and in two different ultrafine grained (UFG) conditions processed by Equal Channel Angular Pressing (ECAP) for 2 and 6 passes at 100o C. Strain rate jump tests in compression were performed at different temperatures and the strain-rate sensitivity exponent m was determined. The tests were accomplished by microstructural investigations before and after compression testing in CG and UFG conditions. It is shown that all UFG microstructures exhibit strongly increased strain-rate sensitivity (SRS) compared to the CG state. The SRS increases with increasing temperature and is more pronounced for the UFG material processed using 6 ECAP passes. The microstructural investigations show a rather high stability of the grain structure for the UFG conditions up to 250o C. The results are discussed with respect to the relevant deformation mechanisms.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.