Strain and damage sensing in additively manufactured CB/ABS polymer composites

Abstract

In this study, an experimental investigation is performed to observe the electromechanical response of CB (carbon black)/Acrylonitrile butadiene styrene (ABS) additive manufactured composite under quasi-static (tensile, shear, and mode-I fracture) and dynamic (mode-I fracture) loading conditions for the potential damage sensing applications. Dog bone tensile, double v-notch shear, and single edge notch bending (SENB) specimen printed with three different configurations (0°/90°, +45°/-45°, and 0°) are considered for the quasi-static condition. A modified split Hopkinson pressure bar along with high-speed video camera is used for dynamic fracture experiments. Four-point probe technique coupled with a high-resolution data acquisition system is employed to obtain the real-time electrical response. In the case of tensile loading, +45°/-45° printed specimens show a nonlinear change of electrical resistance due to unique failure mode. Under the shear loading, electrical resistance remains unchanged during the elastic deformation. After the damage evolution, +45°/-45° printed specimens exhibit a higher rate of change in electrical resistance due to alignment of the filaments along the maximum principle shear stress direction. For both static and dynamic fracture loading, a minimal change of electrical resistance is observed before crack initiation. However, after the crack initiation, a sharp change of electrical resistance for 0°/90° printed specimens indicates a faster crack propagation as compared to the +45°/-45° printed specimens.