Abstract
One of most debated aspects around Nitinol quality is microcleanliness, nowadays considered as the main factor affecting fatigue life. Recent results demonstrate that fatigue is undoubtedly associated with inclusions which can act as crack initiators. However, type, size, and distribution of such particles have been observed to strongly depend on Ni/Ti ratio as well as melting and thermo-mechanical processes. Therefore, if a general reduction of non-metallic inclusions is expected to generate a beneficial effect in improving lifetime of Nitinol, on the other hand this necessarily involves a hard review of both material melting and processing. In this work, the characterization of the fatigue behavior of SMA wires with diameter below 100 µm is presented. The wires were prepared by a peculiar, non-standard combination of melting and thermo-mechanical processes (Clean Melt technology). Thermo-mechanical cycling was carried out and the fracture surfaces of all failed wires were investigated by scanning electron microscopy. A robust set of data was collected and analyzed by using the statistics of extremes. Results clearly demonstrate that in the new NiTi Clean Melt alloy the maximum inclusion size and area fraction are significantly reduced compared to standard Nitinol. This offers meaningful improvement in fatigue resistance over standard wires.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.