Stimuli–responsive track-etched membranes via surface-initiated controlled radical polymerization: Influence of grafting density and pore size

Abstract

The surface-functionalization of poly(ethylene terephthalate) track-etched membranes of different nominal pore sizes (400, 1000 and 3000 nm) with stimuli–responsive poly(2-dimethylaminoethyl methacrylate) (PDMAEMA) via surface-initiated (SI) atom transfer radical polymerization (ATRP) was performed. Variations of grafting density and grafted chain length were achieved by variation of synthesis conditions. It could be clearly demonstrated that mixtures of reaction solutions containing different ratios of acyl bromides, only one bearing the initiator group necessary for the SI ATRP, led to different initiator group densities on the resulting track-etched membrane surface which had been verified by X-ray photoelectron spectroscopy. Moreover the mass increase as function of reaction time strongly correlated with the amount of initiator bound to the membrane surface indicating that the ATRP reaction was not limited by monomer diffusion into the pores. Scanning electron microscopy images and permporometry measurements indicated an even functionalization on the entire membrane surface which was the basis for further investigations. The stimuli–responsive properties of PDMAEMA grafted track-etched membranes were studied by permeability measurements with citrate and glycine buffers as function of pH (2 and 10) and temperature (25 and 60 °C). By that the barrier properties of the membranes could be effectively changed in two steps. The results agree with the expectation that a change in grafting density and chain length has an effect on the stimuli–responsive properties of the membrane. Results for membranes having similar degrees of grafting clearly showed that the reversible swelling of grafted polymeric layers was more pronounced for lower grafting density.