Abstract
A glass of 47.5BaO · 47.5B2O3 · 5Al2O3 (in mol%) having a shorter optical absorption edge (∼236 nm) and suitable glass formation was selected as the mother glass for studying the surface crystallization of β−BaB2O4 · β−BaB2O4 was not the main surface crystallized phase when only a conventional heat treatment was applied. Crystallization of β−BaB2O4 was stimulated due to ultrasonic surface treatment with an ethanol suspension of β−BaB2O4 particles and subsequent heat treatment. After the ultrasonic treatment, β−BaB2O4 was the main crystallized phase. Transparent and dense β−BaB2O4 thin films/glass showed second harmonic generation. The tensor components of the second-order nonlinear optical susceptibility were estimated.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.