Abstract
A Ni-30 mass% Fe alloy with dispersed coarse oxide particles, ranging from 1 to 3 μm in diameter, was multi-directionally forged (MDF) at temperatures between 773 K and 873 K at a true strain rate of 1 x 10-3 s-1 in vacuum. For comparison, a particle-free Ni-Fe alloy was also prepared and MDFed. At 873 K, an obvious flow softening occurred during MDF especially in the alloy with dispersed particles, while work hardening followed by steady-state flow appeared at 773 K in both alloys. With increasing cumulative strain, the average grain size became gradually finer. However, the evolved microstructure was quite different depending on temperature and dispersion of particles. At 873 K, in the alloy with particles, equi-axed fine grains of about 1.3 μm in average was uniformly evolved at a cumulative strain of Σε = 2.4, while at 773 K the microstructure was still inhomogeneous. The above experimental results suggest important role of coarse particles to stimulate grain refinement.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.