Abstract
Engines for marine are subjected to synergistic chloride corrosion and hot oxidation. Here, we fabricated the Ti-Al-N multilayer coatings on TC4 substrate by multi-arc ion plating. The corrosion behavior of coating was conducted under the stimulated environment with 20 cycles of salt spray (35 ℃ for 22 h) and hot corrosion (500 ℃ for 2 h). Result showed that the vast majority of corrosive products were accumulated with increasing corrosion cycles, causing the substantial spallation and delamination of coating. However, the unique structures composing of TiAlN columnar crystals and TiN-Ti-TiN equiaxial crystals still benefited the excellent protective performance for coating.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.