Abstract
ABSTRACT P91 and P92 steels are widely used in power plants and petrochemical industry for long-term service components. Due to high resistance to creep, fatigue and corrosion, the use of grade 91 and grade 92 steels allows ultrasupercritical conditions (600 °C, 300 bar). To achieve this goal the alloy design was based on the following metallurgical concepts: stable tempered martensitic microstructure, precipitation strengthening through M23C6 (Cr, Fe, Mo or W carbides) and fine MX (V, Nb carbides), solution hardening through elements as Mo or Mo/W and high Cr content. This study is focused on the microstructure evolution of grade 91 and grade 92 steels under aging and creep conditions. Three sets of laboratory-aged specimens heated in oven at 550°C, 600°C and 650°C were examined. Furthermore, the influence of stress on the microstructure was evaluated. The microstructures were characterized by several means of investigations and the results were compared to literature.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.