Abstract
In steel–concrete composite structures, stud connectors are applied to achieve the composite action between steel beam and concrete slab. For sea-crossing suspension bridges and cable-stayed bridges, hogging moment regions spread over the full span, which induces tensile stress and unexpected cracking in concrete slabs. Stud connectors embedded in cracked concrete slabs are confronted with higher damage risk induced by atmospheric corrosion. This study investigated the static and fatigue behaviors of corroded stud connectors in weathering steel–concrete composite beams through accelerated corrosion and push-out tests. The ultimate shear strength and load-slip relationship of studs are correlated with corrosion defects on studs. Test results from 15 fatigue push-out specimens indicate a fatigue life reduction up to 80% for corroded studs, basically attributed to accelerated crack initiation from corrosion pits. S-N curves with confidence levels are derived and applied for safety assessment on existing codes. An analytical model reflecting the effect of corrosion is proposed for fatigue life prediction. Evolution of plastic slip and elastic stiffness throughout the fatigue life of studs is further evaluated and the empirical model of residual static performance with a given load history is formulated.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.