Abstract
Abstract The results of investigations of spent moulding sands taken from the mould at various distances from the surface of the produced casting, are presented in the paper. The casting mould was made with an application of the cooling system of the metal core in order to increase the cooling rate of the ladle casting. As temperature measurements in the mould indicated the heat flow from the metal did not create conditions for the complete burning of a moulding sand. The analysis was performed to find out changes of spent moulding sands caused by degradation and destruction processes of organic binders. Conditions occurring in the casting mould were discussed on the bases of testing: ignition losses, dusts contents, pH reactions and the surface morphology of the moulding sand samples. Factors limiting the effective mould degassing were pointed out. Operations, possible for realization, which can limit the reasons of a periodical occurrence of increased amounts of casting defects due to changing gas evolution rates being the result of the technological process, were also indicated.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.