Abstract
The kinetics and formation mechanism of doped corundum (α�Al 2O3) from hydrargillite (γ�Al(OH) 3) in supercritical water fluid (SCWF) in the presence of manganese ions are studied. It was ascertained that due to the reversible dehydroxylation in an aqueous medium, solidphase transformation of hydrargillite into boehmite (γ�AlOOH) and then into corundum occurs with the formation of wellfaceted corundum micro� crystals that are uniformly doped with manganese. It was found that when Mn 2+ or ions are intro� duced into the reaction medium, Mn 5+ , Mn 4+ , Mn 3+ , and Mn 2+ ions are observed in the synthesized corun� dum. Meanwhile, the manganese ions form a complex defect in the corundum structure, which comprises oxygen vacancies and hydroxyl groups. The defects in corundum that emerge upon doping with manganese in SCWF are different from those in corundum doped during hightemperature synthesis.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.