Abstract
ABSTRACTHighly porous SiC ceramics containing borax decahydrate were produced by a starch consolidation method in which corn starch was used as a shaping and pore-forming additive. Four different compositions were prepared with different SiC:borax decahydrate ratios and corn starch content. Mixtures with a solid ratio of 55 wt.% were cast in non-porous molds and heated at 80°C for shaping. The starch consolidation technique enabled the shaping of SiC ceramics with different forms and sizes. Simultaneous thermogravimetry and differential thermal analysis of the SiC-borax decahydrate mixture showed that melting took place at below 600°C, as a result of which sintering was carried out at the relatively low temperature, of 600°C in the air using borax decahydrate as a sintering additive. Phase analysis showed that oxidation of SiC did not take place, since no cristobalite phase was detected. Density measurement and mercury porosimetry studies showed that highly porous (70–89% porosity) SiC ceramics with pore size values ranging from 14 to 18 μm were produced. SEM microstructures of each composition revealed that a strong neck had been formed between the SiC particles in spite of the low sintering temperature.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.