Star polymers by ATRP of styrene and acrylates employing multifunctional initiators

Abstract

AbstractMultifunctional initiators for atom transfer radical polymerization (ATRP) are prepared by converting ditrimethylolpropane with four hydroxyl groups, dipentaerythritol with six hydroxyl groups, and poly(3‐ethyl‐3‐hydroxymethyl‐oxetane) with ∼11 hydroxyl groups to the corresponding 2‐bromoisobutyrates or 2‐bromopropionates as obtained by reaction with acid bromides. Star polystyrene (PS) is produced by using these macroinitiators and neat styrene in a controlled manner by ATRP at 110 °C, employing the catalytic system CuBr and bipyridine. Mn up to 51,000 associated with narrow molecular weight distributions (PDI < 1.1) are obtained with conversions up to 32%. Hydrolysis of the star‐PS leads to linear chains having the expected Mn values. The star‐PS polymers based on dipentaerythritol degrade thermally in nitrogen in a two‐step process in which the first low‐temperature step involves scission of the ester linkages and the second step corresponds to the normal PS degradation. Star poly(methyl acrylates) with various cores are likewise prepared in a controlled manner by ATRP of methyl acrylate in bulk and in solution at 60–80 °C with the 1,1,4,7,7‐pentamethyldiethylene triamine ligand. Under these conditions, higher conversions were possible still maintaining low PDI signaling controlled star growth. Multiarm stars of poly(n‐butyl acrylate) and poly(n‐hexyl acrylate) with controlled characteristics have also been prepared. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 3748–3759, 2005