Abstract
Mass production of alumina-zirconia and alumina-yttria stabilized zirconia nanocomposites powder was prepared from nitrate precursors using an automated hot-air spray pyrolysis technique. The microstructural characteristics of nanocomposites were comprehensively analyzed. X-ray diffraction patterns showed that completely a tetragonal-zirconia phase was stabilized in the nanocomposites at elevated temperature. The average crystallite size for the corresponding nanocomposites powder was measured respectively in the range of 6–65 and 10–47 nm. The produced large quantity of nanopowder was discovered as controlled particle size (d50) of 30 nm, spherical shape, and free flowing structure had a surface area of 61 m2g−1. Further, their structural phase identification and its transformation were correlated through thermal analyzer and diffraction pattern. The interpretation for an increase in hardness and decrease in elastic modulus values of nanocomposites was witnessed at a wide range of calcination. Finally, the t-ZrO2 toughened nanocomposites was retained their overall specific properties and same will be more viable for various industrial applications.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.