Abstract
Fine film-like stable retained austenite was obtained in a Fe–0.08C–0.5Si–2.4Mn–0.5Ni in weight percent (wt.%) steel by the two-step intercritical heat treatment. The first step of intercritical annealing creates a mixed microstructure of preliminary alloy-enriched martensite and lean alloyed intercritical ferrite, which is called as “reverted structure” and “un-reverted structure”, respectively. The second step of intercritical tempering is beneficial for producing film-like stable reverted austenite along the reverted structure. The stabilization of retained austenite was studied by using scanning electron microscopy (SEM), transmission electron microscopy (TEM), dilatometry and X-ray diffraction (XRD) analysis. The two-step austenite reverted transformation associated with intercritical partition of C, Mn and Ni is believed to be the underlying basis for stabilization of retained austenite during the two-step intercritical heat treatment. Stable retained austenite is not only beneficial for high ductility, but also for low temperature toughness by restricting brittle fracture. With 10% (volume fraction) of retained austenite in the steel, high low temperature toughness with average Charpy impact energy of 65J at −80°C was obtained.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.