Abstract
Precipitation behaviour of Al–Mg–Si alloys, with balanced (Mg/Si=2), excess silicon (Mg/Si 2) compositions, were studied by differential scanning calorimetry (DSC), transmission electron microscopy (TEM), and Vickers hardness tests. Four significant exothermic peaks were observed in DSC curves which were attributed to metastable clusters, β″, β′ and stable β phases. The peaks corresponding to β″ and β′ were formed closely in the DSC curves but showed different behaviour in isothermal annealing. The additional peak verifying the precipitation of phases, which has recently been proposed by some workers, was not detected. Transmission electron microscope observations and Vickers microhardness tests showed that β″ precipitates played a major role in improving the hardness, but not β′ precipitates. © 1998 Chapman & Hall
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.