以硝酸锶、硝酸铋和钛酸丁酯为原料，柠檬酸为配位剂，乙二醇为溶剂，用Pechini溶胶–凝胶法制备了SrBi4Ti4O15粉体。研究了柠檬酸量、溶液pH值、乙二醇用量、煅烧温度对产物物相的影响。对所合成粉体进行形貌分析和光催化性能测试。经多组对比试验表明，在pH = 7.0、金属离子：柠檬酸 = 1:3、柠檬酸：乙二醇 = 1:2、干凝胶在650℃煅烧3 h可以得到单相SrBi4Ti4O15粉体。产物SrBi4Ti4O15的结构较疏松，带宽为3.01 eV，在金卤灯下照射3.5 h对甲基橙的降解率可达96.6%。 SrBi4Ti4O15 was prepared by a Pechini sol-gel method, using strontium nitrate, bismuth nitrate penthydrate and tetrabutyl titanate as raw materials, citric acid as ligand, and ethylene glycol as solvent. The influences of the amount of citric acid, pH, ethylene glycol and calcining temperature on the phases of the product were researched. The morphology and photocatalytic properties of the as-synthesized powders were measured. The multiple comparison tests showed single phase of SrBi4Ti4O15 was obtained under the conditions of pH = 7, metals:citric acid = 1:3, citric acid:glycol = 1:2, calcining the dry gel at 650C for 3 h. The as-synthesized SrBi4Ti4O15 had a loose structure with a bandwidth of 3.01 eV. The degradation ratio of methyl orange reached up to 96.6% under the metal halide lamp irradiation for 3.5 h.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.