Abstract
Different crystalline phases in sputtered TiO2 films were tailored to determine their surface and electrochemical properties, protein adsorption and apatite layer formation on titanium-based implant material. Deposition conditions of two TiO2 crystalline phases (anatase and rutile) were established and then grown on commercially pure titanium (cpTi) by magnetron sputtering to obtain the following groups: A-TiO2 (anatase), M-TiO2 (anatase and rutile mixture), R-TiO2 (rutile). Non-treated commercially pure titanium (cpTi) was used as a control. Surfaces characterization included: chemical composition, topography, crystalline phase and surface free energy (SFE). Electrochemical tests were conducted using simulated body fluid (SBF). Albumin adsorption was measured by bicinchoninic acid method. Hydroxyapatite (HA) precipitation was evaluated after 28 days of immersion in SBF. MC3T3-E1 cell adhesion, morphology and spreading onto the experimental surfaces were evaluated by scanning electron microscopy. Sputtering treatment modified cpTi topography by increasing its surface roughness. CpTi and M-TiO2 groups presented the greatest SFE. In general, TiO2 films displayed improved electrochemical behavior compared to cpTi, with M-TiO2 featuring the highest polarization resistance. Rutile phase exhibited a greater influence on decreasing the current density and corrosion rate, while the presence of a bi-phasic polycrystalline condition displayed a more stable passive behavior. M-TiO2 featured increased albumin adsorption. HA morphology was dependent on the crystalline phase, being more evident in the bi-phasic group. Furthermore, M-TiO2 displayed normal cell adhesion and morphology. The combination of anatase and rutile structures to generate TiO2 films is a promising strategy to improve biomedical implants properties including greater corrosion protection, higher protein adsorption, bioactivity and non-cytotoxicity effect.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.