Abstract

PEO-based non-isocyanate polyhydroxyurethane (NIPU, PHU) networks physically modified with octa(3-hydroxy-3-methylbutyldimethylsiloxy)POSS (8OHPOSS) were synthesized via one-pot one-step approach. POSS was introduced into the polymer matrix in the amount of 1–10 wt%. Polar hydroxyls on the vertex groups of POSS allowed for uniform dispersion even up to high loadings (10 wt%). Composites exhibit enhanced thermal stability in comparison to the pristine matrix. FTIR analysis confirmed that POSS strengthens the hydrogen bonding in the material. Upon POSS introduction, plasticization was observed with a peculiar trend change at POSS loadings over 5 wt%. Glass transition temperature of highly crystalline 8OHPOSS was measured and reported to be at around 3 °C. NIPUs at hand exhibit high water absorption (around 200 wt%) typical for hydrogels. Swelling studies show that 8OHPOSS enhances PHUs hydrogels absorption capacity in phosphate-buffered saline (PBS). Higher absorption capacity in PBS solution in comparison to distilled water is an uncommon phenomenon in hydrogels.

Full Text
Published version (Free)

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call