Spectroscopic and electrical studies on Nd3+, Zr4+ ions doped nano-sized BaTiO3 ferroelectrics prepared by sol–gel method

Abstract

Lead free ferroelectric ceramics in the form of Ba(1−3x)Nd(2x)Ti(1−y)ZryO3 ((where x=0.025, y=0 (BT1), 0.025 (BT2), 0.05 (BT3)) were prepared using sol–gel method. The surface morphology and the orientation of grains of the present ceramics were examined using Field Emission Scanning Electron Microscope (FESEM) images. The effect of Nd3+, Zr4+ ions content on the BaTiO3 was studied using Raman and Fourier Transform Infrared (FTIR) spectroscopies. From the Raman analysis the band observed at ∼838cm−1 was attributed due to the presence of Nd3+-barium vacancy pairs. The FTIR studies suggested that the addition of Nd3+ ions in A-site of BaTiO3 (ABO3) perovskite create lattice distortion by forming A-site vacancies and Zr4+ ions in B-site of BaTiO3 induce the lattice distortion by forming ZrO6 octahedra in the place of TiO6 octahedra. Dielectric measurements of the samples were done at different frequencies from RT-150°C. Charge transportation phenomenon is explained using DC conductivity, which is found to increase with temperature.