Abstract
The spectral emission study of the radioluminescence (RL) measured from carbon-doped aluminium oxide (α-Al2O3:C) at various temperatures between 30 and 300∘C is reported. The energy-resolved RL emission spectra measured at room temperature show seven gaussian emission bands centred at 1.75, 1.79, 1.85, 2.22, 2.96, 3.72 and 4.44 eV. The 2.96-eV emission, associated with F-centres, is the primary RL emission whereas the narrow (R-line) emission centred at 1.79 eV, associated with Cr3+ impurity ions, is the most intense secondary emission. However, the intensity of 1.79-eV emission decreases with repeated RL measurements. The central emission energy for F-centres is constant throughout the temperature range of investigation. The full width at half maximum (FWHM) for the F-centre emission band increases with temperature whereas the F-centre peak intensity exhibits thermal quenching behaviour at temperatures above 160∘C. On the other hand, the emission energy for the R-line emission of Cr3+ is constant for temperatures between 30 and 160∘C, whereas its peak intensity generally decreases with temperature. F-centres experience strong-coupling in their crystallographic sites with estimated electron-lattice coupling parameters of S = 5.0 ± 0.9, Ep = 0.079 ± 0.008 eV and ν = 1.91 × 1013 Hz where S, Ep and ν are the Huang-Rhys factor, the phonon energy and the phonon frequency, respectively. The RL spectra recorded while ramping the temperature of a sample at a constant rate have been compared against conventional TL spectra.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have