ABSTRACTTi5Al2.5Fe alloys were fabricated by the spark plasma sintering (SPS) and hot pressing (HP) pressure-assisted sintering techniques from pre-alloyed powders with a particle size of about 200 μm. The powders were sintered at 850 °C for two different holding times (5 and 8 min) and heating rates (50 and 150°C min−1) at 25 MPa. The maximum relative densities were 99.70 and 98.78% for SPS and HP samples, respectively. All the alloys prepared by the SPS process had significantly higher bending strengths (1825–2074 MPa) than the alloys prepared by the HP process (648–1330 MPa). A decrease in the heating rate from 150 to 50°C min−1 enhanced the wear resistance of the Ti5Al2.5Fe alloys prepared by both the SPS and HP processes.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.