Abstract
Densification of alumina whisker-reinforced alumina ceramics by spark plasma sintering (SPS) has been investigated with the aim of obtaining a fine-grained microstructure and also studying the effect of whisker addition on the room-temperature mechanical properties. It was found that whisker addition retards slightly the sinterability of alumina by whisker hindering of particle rearrangement. Besides, the internal stress on the alumina matrix particles reduced due to the presence of a whisker network structure of strong rigid boundaries. Nevertheless near fully-dense and fine-grained alumina ceramics with alumina whisker content between 3wt% and 10wt% could be obtained under appropriate SPS conditions. The hardness of alumina ceramics with 3wt% was comparable to that of pure alumina ceramics (∼26GPa) whereas its fracture toughness (5.6MPam1/2) was higher (4.2MPam1/2). Crack bridging by well-dispersed whiskers and whiskers pull-out were identified as the main toughening mechanisms.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call