Abstract
The aim of this study was to produce dense and mechanically strong boron carbide ceramics with the help of different oxide additives. Physical properties of two different grades of pure boron carbide powders were analysed and sintered by Spark Plasma Sintering method. Starting powders were prepared by ball milling with the addition of 5 wt. % Y2O3, Al2O3, SiO2 and Y2O3 + Al2O3. In the sintering step, powder mixtures were sintered by SPS method in round-shaped graphite dies under 50 MPa for 5 minutes in the range of 1700-1800oC. In the characterization step, sintered sample compositions and microstructures were characterized by XRD and SEM analysis respectively. The hardness values were measured under 1000 g load and the density values were measured with Archimedes' principle. The fracture toughness analysis were also carried out.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.