Abstract
An attempt was made to produce continuous fiber reinforced titanium matrix composites using spark plasma sintering machine from foils and fibers. The materials used were metastable beta titanium alloy Ti-15V-3Cr-3Al-3Sn foils (125µm thick) and silicon carbide fibers (100µm in diameter). The method involved consolidating foils with fibers placed in between them at regular intervals. After a series of trials, the feasibility of the process was established. Spark plasma consolidation enabled satisfactory foil bonding and fiber embedment at a significantly lower temperature and time compared to conventional diffusion bonding or vacuum hot pressing. The composite samples consolidated above the beta-transus temperature of the titanium alloy were found to develop satisfactory strengthening precipitation upon direct aging. The current study shows that spark plasma consolidation is an excellent alternative to conventional diffusion bonding for producing continuous fiber reinforced titanium matrix composites.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.