Space charge behavior in polymer film based on increment of capacitance under AC high field

Abstract

AbstractPolymer materials have excellent dielectric and insulation properties; however, those properties in AC high field region have not been known well. Recently we established an evaluation method of high‐field AC dissipation current waveform of polymer materials 1. AC dissipation current waveforms of polyethylene and polypropylene films show nonlinear distortion in AC high‐field region. This nonlinearity was thought to be related to the behavior of AC space charge formation in the sample near electrodes. The properties of space charge formed under AC high field at power frequency seem to differ from those formed under DC high field. The measurement of AC space charge distribution is not so easy due to the resolution limit of the space charge measurement.We studied the dielectric properties of biaxially oriented polypropylene (BOPP) film under AC high field up to 120 °C. It was found that tan δ, AC dissipation current (Ixr), and unbalanced component of capacitive current (ΔIxc) increased when the temperature became higher. In particular, ΔIxc increased above some threshold field and was considered to be due to the AC space charge formation. This AC space charge layer near electrode is thought to be formed due to carrier injection under AC high‐field application. Usually, the carrier mobility becomes smaller on lowering the temperature. Most of the carriers injected from the electrode are trapped near the electrode in the sample film. But in the high‐temperature region, the carrier mobility becomes larger and the carrier injection starts to increase from lower field. Many more carriers are injected from the electrode. It is thought that some of the injected carriers are trapped inside the sample film; the others go through the sample to the opposite side. © 2002 Wiley Periodicals, Inc. Electr Eng Jpn, 141(2): 8–16, 2002; Published online in Wiley InterScience (www.interscience.wiley.com). DOI 10.1002/eej.10018