Abstract
A space-charge-limited beam with current densities (J) exceeding 1 mA/cm(2) have been measured from lithium alumino-silicate ion sources at a temperature of ∼1275 °C. At higher extraction voltages, the source appears to become emission limited with J ≥ 1.5 mA/cm(2), and J increases weakly with the applied voltage. A 6.35 mm diameter source with an alumino-silicate coating, ≤0.25 mm thick, has a measured lifetime of ∼40 h at ∼1275 °C, when pulsed at 0.05 Hz and with pulse length of ∼6 μs each. At this rate, the source lifetime was independent of the actual beam charge extracted due to the loss of neutral atoms at high temperature. The source lifetime increases with the amount of alumino-silicate coated on the emitting surface, and may also be further extended if the temperature is reduced between pulses.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.