Some Lewis acid-base adducts involving boron trifluoride as electrolyte additives for lithium ion cells

Abstract

Abstract Three complexes with boron trifluoride (BF3) as the Lewis acid and different Lewis bases were synthesized and used as electrolyte additives in Li[Ni1/3Mn1/3Co1/3]O2/graphite and Li[Ni0.42Mn0.42Co0.16]O2/graphite pouch cells. Lewis acid-base adducts with a boron-oxygen (B O) bond were trimethyl phosphate boron trifluoride (TMP-BF) and triphenyl phosphine oxide boron trifluoride (TPPO-BF). These were compared to pyridine boron trifluoride (PBF) which has a boron-nitrogen (B N) bond. The experimental results showed that cells with PBF had the least voltage drop during storage at 4.2 V, 4.4 V and 4.7 V at 40 °C and the best capacity retention during long-term cycling at 55 °C compared to cells with the other additives. Charge-hold-discharge cycling combined with simultaneous electrochemical impedance spectroscopy measurements showed that impedance growth in TMP-BF and TPPO-BF containing cells was faster than cells containing 2%PBF, suggesting that PBF is useful for impedance control at high voltages (>4.4 V). XPS analysis of the SEI films highlighted a specific reactivity of the PBF-derived SEI species that apparently hinders the degradation of both LiPF6 and solvent during formation and charge-hold-discharge cycling. The modified SEI films may explain the improved impedance, the smaller voltage drop during storage and the improved capacity retention during cycling of cells containing the PBF additive.