Abstract
AbstractBarrier formation and increasing the melt viscosity are addressed as the two main general fire retardancy mechanisms of polymer nanocomposites. They result in specific impacts on fire properties that consequentially cause varying flame retardancy efficiency in different fire tests. The barrier formation retards mainly flame spread (peak of heat release rate) in developing fires, but does not reduce fire load (total heat evolved), ignitability or flammability (limiting oxygen index, UL 94). Furthermore, this flame retardancy effect increases with increasing irradiation and vanishes with decreasing irradiation. The increased melt viscosity prevents dripping, which is beneficial or disadvantageous depending on the fire test used. In some test, it become the dominant influence, transforming self‐extinguishing samples into flammable materials or causing wicking. Advantages and the limits are sketched comprehensively for exploiting the main general fire retardancy mechanisms of polymer nanocomposites. It is concluded that barrier formation and changing the melt viscosity in nanocomposites are not sufficient for most applications, but must be accompanied by additional mechanisms in special systems or in combination with other flame retardants. Copyright © 2006 John Wiley & Sons, Ltd.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.